Product Specification

February 2016

Material Specification

Envelope Material

CLL-S High optical quality clear

gloss PVC suited to silkscreen,

with high impact strength

Self-adhesive Fixing

Closed cell polyethylene cross

linked foam

Temperature range: -40oC to 90oC

(when applied at ambient)

Magnetic Fixing

Isotropic Magnetic Flexible

Extrusion (Matched Poles)

comprising of strontium ferrite

in a synthetic rubber binder and

magnetized multi-pole on one face.

Flexibility: At 20oC can be curved

to 25mm radius without cracking.

Features and Benefits

• Enables documents to be

framed and displayed

• Available in sizes to fit A2, A3,

A4 and A5

• Magnetic and self-adhesive

fixing available

frames4docs®

Document Display

Temperature range: -30oC to 55oC (above 50oC magnetic losses

occur). Attached with modified acrylic adhesive polyester tape,

temp range -30oC to 175oC. Adhesion @70oC: 20N/20mm.

Adhesive type

Modified acrylic

Both faces

Tape thickness (no liner)

1.5 mm

Release liner type/colour

Siliconised brown paper

0.075mm thick

Foam density

67 kg M3

Peel adhesion @23°C

22 n/ 25mm

To foam tear

Peel adhesion @70°C

14 n/25mm

To foam tear

Shear @23°C

400+ hours

1kg on 25mm2

Ageing and UV resistance

Excellent and Good

Shelf life

2 years

@ 20°C, 65%RH

Parameter

Specification

Test Method

Thickness

> 300 - 950μm ± 5%

Density

1.32 ± 0.01 g/cm³

ASTM D-792 DIN53479

Vicat softening point

1kg / in oil / as stacked samples

72 ± 2oC

ISO 306-A50

Vicat softening point

5kg / in oil / as stacked samples

81 ± 2oC

ISO 306-A50

Tensile yield strength (MD)

44 ± 3 N/mm2

ISO 527

Elongation at yield (MD)

6 ± 1%

ISO 527

Tensile strength at break (MD)

35 ± 3 N/mm2

ISO 527

Elongation at break (MD)

> 50%

ISO 527

Impact test

> 600 KJ/m2

ISO 8256

Elongation at impact

13 ± 2mm

ISO 8256

Water absorption

0.04 ± 0.02%

ASTM D-570 DIN53495